TU 14-3R-55-2001 Seamless steel pipes for steam boilers and pipelines |
|
|
Standard: TU 14-3R-55-2001
Equivalent Standard: DIN 17175, EN 10216-2 |
Material: 12Ch1MF-PV
Equivalent Materials: 12Cr1MoVG |
Chemistry Composition |
C, % |
Si, % |
Mn, % |
P, % |
S, % |
Cr, % |
Mo, % |
V, % |
Ni, % |
Cu, % |
0.11-0.15 |
0.17-0.37 |
0.40-0.70 |
0.015 max |
0.025 max |
0.90-1.20 |
0.25-0.35 |
0.15-0.30 |
0.15 max |
0.15 max |
|
Mechanical Properties |
Tensile Strength , MPa |
Yield Strength, MPa |
Elongation, % |
441-637 |
274 min |
21 min |
|
Outside Diameter & Tolerance |
Hot rolled |
Outside Diameter, mm |
Tolerance, % |
Normal |
High |
OD<50 |
±0.40mm |
- |
50≤OD<114 |
- |
±0.75 |
114≤OD<245 |
±1.0 |
±0.9 |
245≤OD<325 |
±1.0 |
±0.9 |
OD≥325 |
+1.25/-1.0 |
±1.0 |
Cold & Warm |
Outside Diameter, mm |
Tolerance, % |
Normal |
High |
OD<30 |
±0.30mm |
- |
30≤OD<50 |
±0.40mm |
- |
50≤OD≤108 |
±0.80mm |
- |
OD>108 |
±0.90mm |
- |
|
Wall thickness & Tolerance |
Hot rolled |
Wall Thickness, mm |
Tolerance, % |
Normal |
High |
OD<50 |
+12.5/-10.0 |
- |
50≤OD<114, WT<7 |
+15.0/-10.0 |
- |
50≤OD<114, 7≤WT≤14 |
+15.0/-10.0 |
+12.5/-10.0 |
50≤OD<114, WT>14 |
+15.0/-10.0 |
±10.0 |
114≤OD<325 |
+20.0/-5.0 |
- |
114≤OD<325 |
+20.0/-5.0 |
+15.0/-5.0 |
OD≥325 |
+20.0/-5.0 |
- |
OD≥325 |
+20.0/-5.0 |
+17.5/-5.0 |
377≤OD≤530, 25≤OD≤90 |
+20.0/-5.0 |
- |
Cold & Warm |
Wall Thickness, mm |
Tolerance, % |
Normal |
High |
OD<108 |
±10 |
- |
OD≥108 |
+15.0/-5.0 |
- |
|
Length: 4000mm; 8030mm; 8050mm; 12010mm; 12030mm; 12050mm; and so on.
Max developed length: 30 meters, also U bending, finning, studded process can be provided.
Option: shot blasting on the outside surface to remove mill scale, make the surface matte colour; surface polishing as preparation work done for further processing, for instance finning. |
Keyword: boiler steel pipes, seamless steel pipes, seamless steel tubes, ТУ 14-3Р-55-2001, TU 14-3R-55-2001 |
|
|
|
|
|
|
|